Garage Door InsulationGARAGE DOOR LINER
High Impact Polystyrene Laminated to
Expanded Polystyrene
H.I.P. Features - Good environmental stress crack resistance, good paintability, UL Classification
94 HB, USP Class VI H.I.P. Technical Data S.I. UNITS TYPICAL ENGLISH TYPICAL PROPERTIES (1) Mpa VALUES (2) UNITS VALUES (2) ASTM (S.I.) (ENG.) Tensile Strength Yield MPa 21 psi 3,000 D638 Elongation, Failure % 50 % 50 D638 Tensile Modulus MPa psi x 10³ D638 Flexural Strength @ 5% MPa 29 psi 4,200 D790 Flexural Modulus MPa 1,650 psi x 10³ 240 D790 Impact Strength, Notched ft-lb/in of Izod, 1/8" bar, 0.010" J/m 149 notch 2.8 D256 Notch Radius Melt Flow Rate, 200/5.0 g/10 min 3.0 D1238 Vicat Softening Temp. °C 100 °F 212 D1525 Heat Deflection Temp. °C 85 °F 185 D648 1.8 Mpa/264 psi Specific Gravity - 1.04 - 1.04 D792 Linear Mold Shrinkage mm/mm 0.004-0.007 in/in 0.004-0.007 D955 (1) Properties were determined on injection molded specimen at 23° C(73° F) and 50% R.H. unless
otherwise specified. (2) Typical values represent average laboratory value and are intended as guides only, not as specific specification limits EPS Features - Permanent R-Value, dimensionally stable, sound deadening, outstanding resistance to moisture absorption. Standards Compliance - EPS insulation may be manufactured to meet or exceed the requirements of ASTM C578 and applicable building codes.... To read the rest of the content please click the attached pdf. EPS Technical Data
PROPERTY UNITS ASTM TEST TYPE 1 Density pcf, minimum C303 0.90 Thermal Resistance per inch C518 Values (R) thickness At 25F (-3.9 C) 4.20 At 40F ( 4.4 C) 4.00 At 75F (23.9 C) 3.60 Compressive Resistance 10% psi, minimum D1621 10 Deformation Flexural Strength psi, minimum C203 25 Water Vapor perm-in., E96 5.0 Permeability maximum Water Absorption % by Vol Max C272 4.0 by Total Immersion  Garage Door Liner Technical Data Sheet (33 KB)
|
|
||||||||||||||
    |